Moulding materials

ABSTRACT

Moulding material that includes a layer of fibrous reinforcing material having one surface on which a first layer of a resin partially impregnates the fibrous material and a further resin layer located on the opposite surface which retains in position surface fibers of the fibrous material. The further resin layer is of lower weight than the first layer and is formed as an openwork structure with a solid part and spaces through which the fibrous material is exposed.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to composite moulding materials or pre-forms ofresin and reinforcement fiber in which the resin is only partiallyimpregnated into the fiber.

2. Description of Related Art

Such pre-forms are normally supplied in a continuous roll but may alsobe provided as pre-cut sheets. In either case the material may be laidup in multiple layers on a shaped moulding surface, alone or incombination with further resin, and then processed (e.g., by applicationof heat and pressure) to form strong, lightweight structures, e.g., foruse in forming panels or body sections or components in aerospace,automotive, wind energy or other contexts.

The fibrous reinforcing material may be partially or substantially fullyimpregnated with the resin in the pre-form, resulting in a so-calledsemi-preg or pre-preg. The fibrous material advantageously may comprisetows with fibers which are unidirectional, i.e., which extendpredominantly in a common direction, since this facilitates manufactureof strong laminates of high mechanical integrity suited to theproduction of relatively long, large and thick structures such as windenergy blades.

Semi-pregs in which the fibrous material is only partiallyresin-impregnated so as to leave a ‘dry’ outer surface, i.e., a surfacehaving free fibers not impregnated by resin, can advantageouslyfacilitate ready release of trapped air during processing whichminimizes void content and consequent mechanical weakening in thefinished product. However, there is the problem that a unidirectionalalignment of the exposed dry fibers on the outer surface tends to becomedisrupted during handling, cutting and laying-up with consequentreduction in mechanical integrity of the finished product. Moreover,contaminant fibrous debris may be produced.

Disruption of fiber alignment can be avoided with conventional pre-pregsdue to the full resin impregnation of the fibrous material, but withthese materials, problems of handling and void content can ariseparticularly when using heavy fiber bundles.

WO 00/27632 provides an example disclosure of a semi-preg which hasexposed dry fibers and which would therefore exhibit the above mentionedfiber-disruption problem.

EP 0583090 A describes sandwiching of fibrous material between resinfilms. The fibrous material is impregnated by the resin matrix whichwould prevent surface disruption of fibers. However, this technique,particularly if used with substantial unidirectional fiber tows, wouldtend to give only partial impregnation thereby leading to air entrapmentin the dry fibers in the center of the pre-form causing voids andconsequent poor mechanical strength in the finished product.

With a view to improving mechanical integrity, it is known tocross-stitch unidirectional fiber tows. This is described in WO98/34979in the context of a semi-preg. However, loose or broken filaments fromthe stitching process can cause performance deterioration in thelaminate and also does not necessarily solve the handling problemsassociated with unidirectional tows.

Warp fiber bundles can be held together in pre-forms with thermoplasticstabilizing yarns. However, if the melting point of the thermoplastic ishigher than the processing temperature of the pre-form resin matrix, theyarns can give rise to fiber distortion, and hence poor mechanicalproperties, where the weft yarns are crimped over the warp. If thethermoplastic has a lower melting point than the resin matrix processingtemperature, the thermoplastic melts and flows into the resin matrixproducing voids in the finished product.

U.S. Pat. No. 6,096,669 describes the formation of a pre-form obtainedby sandwiching unidirectional fiber tows between resin films which arein the form of openwork diamond-pattern grids. The grids act to hold thefibers in position but are relatively insubstantial and a resin matrixis introduced externally by penetration through the grids using aconventional so-called resin transfer moulding process. Such processesare used for production of relatively small, short length structures andare not appropriate for larger, longer length structures, where adequateresin flow along the fiber pre-form cannot be ensured.

U.S. Pat. No. 4,213,930 describes the use of a gravure roll to applysmall amounts of resin to the surface of a pre-preg to improve surfacetack on a fully impregnated pre-form.

SUMMARY OF THE INVENTION

An object of the present invention is to provide a semi-preg pre-formhaving dry surface fibers which are reliably held in position in animproved manner conducive to production of composites having highmechanical integrity.

According to the invention therefore there is provided a mouldingmaterial comprising a layer of fibrous reinforcing material having onopposite surfaces thereof, respectively, a first layer of resin whichpartially impregnates the fibrous material, and a further resin layerwhich retains in position surface fibers of the fibrous material,characterized in that the further resin layer is of lower weight thanthe first layer and is formed as an openwork structure with spacesthrough which the fibrous material is exposed.

With this arrangement, the moulding material is of the nature of asemi-preg, due to the first resin layer, whereby the moulding materialcan be processed to form structures without requiring significantintroduction of an externally introduced resin matrix. Moreover, theopenwork further resin layer can hold surface fibers of the fibrousmaterial securely and smoothly in position without restricting air flowfor escape of entrapped air.

The moulding material is therefore particularly suitable for use inproducing relatively large, long structures which are substantiallyvoid-free and have high mechanical strength and integrity.

The above discussed and many other features and attendant advantages ofthe present invention will become better understood by reference to thedetailed description when taken in conjunction with the accompanyingdrawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagrammatic sectional view of one form of a mouldingmaterial according to the invention in accordance with Examples 2-5.

FIG. 2 is a diagrammatic representation of processing equipment used informing the moulding material of Examples 2-5.

FIGS. 3-9 are diagrammatic plan views of exemplary openwork resin layersapplied to the surface of the moulding material.

DETAILED DESCRIPTION OF THE INVENTION

The fibrous reinforcing material is preferably of the unidirectionalkind, i.e., having fibers predominantly extending substantially in acommon direction. Thus, the fibrous material may comprise multipleside-by-side tows, i.e., loose bundles of fibers. The tows and thefibers may all extend in the common direction, or there may be sometransverse fibers. In the latter case, the transverse fibers arepreferably such as to exert little or no positional or dimensionalcontrol on the unidirectional fibers.

Most preferably the moulding material is of elongate form particularlyin the form of sheeting or a strip or tape. Preferably, also, whereunidirectional fibrous material is used, the fiber common direction ispreferably the longitudinal direction of the moulding material.

The fibrous material may be formed from any suitable kind of material orcombination of material including synthetic and natural fibers, glass,ceramic, metal and carbon fibers. Materials which may have very smallfilament diameters, such as carbon fibers are specially suitable.

The fibers may be continuous or may have discontinuities and they, forexample, may be stretch-broken or otherwise selectively discontinuous.

Discontinuous fibers can give enhanced drape and formability in thelongitudinal direction. In this case, advantageously, the openworkfurther layer can help avoid movement of loose ends thereby improvingmechanical properties by minimizing misalignment.

The first resin layer is preferably a solid, substantially continuousfilm (i.e., substantially without spaces or openings therein) which maybe sticky or tacky to the touch but is sufficiently coherent and solidas to be self-supporting at normal temperatures. This layer may beformed wholly from resin material or it may incorporate reinforcementsor other materials. In one embodiment the first resin layer may be apre-preg layer.

The resin of the first layer is preferably (although not necessarily) aheat-curable thermosetting resin matrix, and the first layer ispreferably of sufficient quantity to impregnate all or at least a majorpart of the fibrous material during processing of the moulding material,e.g., when subjected to heat and pressure.

The further layer is preferably formed from a resin the same as orsimilar in properties to the resin of the first layer. Thus, the resinof the further layer is preferably sufficiently solid and coherent as tobe self-supporting at normal temperatures and in a heat-curablethermosetting resin matrix. Thus, on processing of the moulding materialthe resin of the further layer may blend smoothly with the resin of thefirst layer without adversely affecting the integrity of the curedcomponent.

With regard to the openwork structure of the further resin layer thismay take any suitable form appropriate to positional retention of thefibers without significantly occluding the surface of the fibrous layer.

Preferably, solid parts of the further layer occupy a minor proportionof the surface area of the fibrous layer, the spaces thereincollectively making up the major part. The solid parts may occupy lessthan 25% of the surface area, say 4% to 24% of the area.

The further layer may comprise linked or continuous solid parts such asa grid pattern of solid linear elements enclosing geometrical spaces, ora perforate web having regular or irregular spaces, which spaces may becircular, hexagonal or any other suitable shape. Alternatively, thefurther layer may comprise wholly separate or discontinuous solid partswhich may be linear elements or other shaped parts, such as parallellines, chevrons, dots, broken lateral lines or the like. Broken linesmay be particularly preferred to facilitate air flow.

The further layer may be applied in any suitable manner. This maycomprise transfer, e.g., via a transfer film, or by direct applicationto the surface. Suitable application techniques include gravureprinting, reverse roll coating, forward roll coating, scatter coating,spraying, powder coating, resin gun or cartridge deposition, etc.

It is also possible to establish the further layer by pull-through ofresin material from the first layer. This may be done by an ultrasonictechnique. This pull through may result in discrete solid parts, i.e.,such that the further layer is separate from the first layer, or linkedsolid parts, i.e., with linking strands extending between the furtherand first layer through the fibrous material.

The amounts and relative proportions of the resin in the first andfurther layers will be selected in accordance with requirement. Mostpreferably, the amount of resin in the first layer is a multiple of theamount in the further layer.

Preferably, the proportion of total resin content for the further layeris up to 5%, most preferably up to 1%, the balance being provided by thefirst layer.

By way of example, the resin of the first layer may amount to 30 to 50%by weight, particularly 35 to 40% of the moulding material, and theresin of the further layer may amount to 0.1 to 20%, more preferably 0.1to 10%.

When the openwork structure is applied from a resin-solvent mixture, theresin content can be controlled to within 0.1-10.0%, more preferably0.1-1.0%. When solvent-free (hot melt) techniques are employed, theresin content can be controlled in the range of 1.0-20%, more preferably0.1-10%.

Thus, the resin in the further layer may be of the order of 1 to 2 gsmor to 30 gsm from a resin solvent mixture or 2 gsm to 60 gsm whensolvent-free (hot melt) resin, and in the first layer of the order of 75to 150 gsm or to 280 gsm, and the moulding material may be 200 or 300 to500 gsm or 700 gsm including the resin and the fibrous material,considered in relation to a single layer of fibrous material and asingle said first resin layer.

Using carbon fiber as the fibrous material areal weight, any range from80 to 6000 gsm, more preferably 100 to 2500 gsm and most preferably 150to 2000 gsm, and the carbon fiber filament count may be 3000 to 320000,more preferably 12000 to 160000 and most preferably 24000 to 80000.

In one example, the moulding material contains 500 gsm carbon fiber, 280gsm first resin layer, and 20 gsm further resin layer. In anotherexample, the material contains 150 gsm carbon fiber, 92 gsm first resinlayer, and 2 gsm further resin layer.

The resin material of the first and/or further resin layers may be anysuitable thermosetting or thermoplastic material, preferablythermosetting.

Thus, the resin may comprise an epoxide resin, bismaleimide, aphenolaldehyde resin or any other suitable resin. Curing agents andother performance enhancing additives such as flame retardants,anti-fouling agents and tougheners may be incorporated.

Mixtures of resins may be used, e.g., a mixture of a thermosetting and athermoplastic resin.

Semi-impregnation of the fibrous material by the resin of the firstlayer may be effected under appropriate temperature and pressure, thetemperature being lower than that required for curing. Typically thetemperature may be in the range 40° C.-160° C., particularly 90°-120°C.; and the pressure may be 40-120 psi (2.7-8.3 bar), particularly80-100 psi (5.5-7.0 bar). These processing conditions will vary for thedifferent combinations of resin and fiber chosen. Methods to measure theextent of resin diffusion into fiber are well known to those in the artand include wicking techniques and microdielectric analysis.

The further layer may be contact applied, i.e., such that it rests onthe surface or lightly impregnates the fibrous material. Thus, this maybe applied at an elevated temperature (below curing temperature) withoutany significant pressure.

The arrangement may be such that the resin of the first and furtherlayers are separate from each other. Alternatively they may contact eachother so as to be interconnected through the fibrous material. This maybe achieved by causing portions of the resin of the first layer toextend through the fibrous material to the surface to which the furtherlayer is applied, without wholly impregnating the entire body of fibrousmaterial.

Advantageously, the invention can be applied to the production of amoulding material having multiple layers with one or two dry faces, oneor both of which may have a respective further resin layer appliedthereto.

In particular, the moulding material of the invention may comprise twolayers of fibrous material with a first resin layer sandwiched betweenand partially impregnating the two fibrous layers, and a furtheropenwork resin layer applied to the outer surface of one or both of thefibrous layers.

The moulding material may have multiple internal layers of anyappropriate materials and construction.

Possible constructions include the following:

In one embodiment a resin rich fully impregnated and unidirectional orwoven pre-preg can be made and used as the said first layer in place ofa film made wholly of resin. Fibrous material, e.g., in the form ofadditional fiber tows can then be placed on top of this film followed bythe openwork resin layer.

In a further embodiment, a resin rich fully impregnated unidirectionalor woven pre-preg can be made and additional fibrous material (e.g.,fiber tows) then placed on both sides of this pre-preg. Openwork resincan then be coated onto both dry fiber surfaces.

In a yet further embodiment, an additional layer of material such as drytextiles, a gel coat film or intumescent can be laminated, e.g., ontothe said first layer.

Also scrims, gauzes, non-wovens, and mats can be incorporated. Typicallythese may be less than 20 gsm in weight.

Many other variations, involving sequential addition of resin-film,fiber and other material layers, are possible. This also permits the useof hybrid fiber layers.

The present invention may find particular application in the context ofrelatively massive long length components such as wind energy blades.However, it is not restricted to this field of application and may beused for aerospace, automotive or other applications.

The invention will now be described further with reference to thefollowing Examples. Example 1 is for comparison purposes. Examples 2-7are in accordance with this invention.

In these Examples reference is made to Hexcel epoxy M9.6. This is aproprietary medium tack formulated epoxy resin which is suitable for lowpressure moulding processes and is available from Hexcel Corporation(Duxford, England). It is very versatile and allows a range ofprocessing temperatures from 75° C. up to 160° C.

M9.1 is a higher tack version of M9.6 that is also available from HexcelCorporation (Duxford, England).

913 is proprietary modified epoxy resin which is available from HexcelCorporation (Duxford, England) and has a typical cure cycle of 1 hour at120° C.

EXAMPLE 1

A semi-pre-preg material was made at 300 mm wide from unidirectionalcarbon fiber tows in sheet form of 150 gsm fiber areal weight and 92 gsmheat curable resin matrix on one face. The fiber used was Fortafil®F510-80K and the resin matrix was Hexcel epoxy M9.6. Additional exampleswere replicated using Tenax® STS-24K fiber and M9.1 resin.

The processing conditions of temperature, pressure and line speed weresuch as to cause the resin matrix to penetrate only partially into thecarbon fiber layer.

The resulting product had a continuous tacky resin layer on one face anddry fibers on the opposite second face. The fibers were aligned in thewarp direction (longitudinally) with no added weft material. The producthad a total weight of 242 gsm with 38% by weight of resin. The secondface was freely exposed and in particular had no resin material appliedthereto.

EXAMPLE 2

A semi-pre-preg material was made in like manner to Example 1 at 300 mmwide with M9.6 resin and F510-80K fiber. In addition, transverse linesof 913 resin were applied to the dry face.

The transverse lines were applied to a release paper using a gavure rolland were then transferred from the paper to the dry face of thesemi-preg. The resin applied to the dry face amounted to 2 gsm.

EXAMPLE 3

A semi-pre-preg material was made at 300 mm wide from unidirectionalF510-80K carbon fiber tows in sheet form of 500 gsm fiber areal weightand 280 gsm heat curable M9.6 resin matrix on one face.

The processing conditions of temperature, pressure and line speed weresuch as to cause the resin matrix to penetrate only partially into thecarbon fiber layer.

Transverse lines of the same M9.6 resin were applied to the dry face.

The lines were applied to a release paper using a reverse roll coatingprocess and were then transferred from the paper to the dry face of thesemi-preg. The resin applied to the dry face amounted to 20 gsm.

EXAMPLE 4

A pre-preg material was made at 300 mm wide from unidirectional F510-80Kcarbon fiber tows in sheet form of 250 gsm fiber areal weight and 280gsm heat curable M9.6 resin matrix on one face.

Processing conditions for this material were such as to cause the resinmatrix to fully impregnate or wet out the tows.

In further steps of the process a dry layer of further unidirectionalcarbon fiber tows in sheet form of 250 gsm fiber areal weight wasapplied to the top surface of the pre-preg thereby forming a semi-pregstructure. Finally, transverse lines of the same resin were applied tothe dry fibrous face defined by the further tows.

The lines were applied to a release paper using a reverse roll coatingprocess and were then transferred from the paper to the dry face of thesemi-preg. The resin applied to the dry face amounted to 20 gsm.

EXAMPLE 5

In similar manner to Example 4, a pre-preg material was made at 300 mmwide from unidirectional F510-80K carbon fiber tows in sheet form of 400gsm fiber areal weight and 280 gsm heat curable M9.6 resin matrix on oneface.

In further steps of the process a dry layer of unidirectional carbonfiber tows in sheet form of 100 gsm fiber areal weight was applied tothe top surface of the pre-preg. Finally, transverse lines of the sameresin were applied to the dry fibrous face.

The lines were applied to a release paper using a reverse roll coatingprocess and were then transferred from the paper to the dry face of thesemi-preg. The resin applied to the dry face amounted to 20 gsm.

EXAMPLE 6

In similar manner to Example 4 a pre-preg material was made at 300 mmwide from unidirectional F510-80K carbon fiber tows in sheet form of 250g/m² fiber areal weight and 280 gsm heat curable M9.6 resin matrix onone face.

In further steps of the process a dry layer of unidirectional carbonfiber tows in sheet form of 125 gsm fiber areal weight was applied toboth surfaces of the pre-preg.

Transverse lines of the same resin were then applied to the dry fibrousfaces on both surfaces of the product. The lines were applied to arelease paper using a reverse roll coating process and were thentransferred from the paper to the dry face of the semi-preg. The resinapplied to the dry face amounted to 20 gsm.

EXAMPLE 7

In similar manner to Example 4, a pre-preg material was made at 300 mmwide from unidirectional F510-80K carbon fiber tows in sheet form of 250gsm fiber areal weight and 280 gsm heat curable M9.6 resin matrix on oneface.

In further steps of the process a dry layer of unidirectional carbonfiber tows in sheet form of 250 gsm fiber areal weight was applied toone surface of the pre-preg. Transverse lines of the same resin wereapplied to the dry fibrous face. The lines were applied to a releasepaper using a reverse roll coating process and were then transferredfrom the paper to the dry face of the semi-preg. The resin applied tothe dry face amounted to 20 gsm.

A continuous film of curable resin matrix for surface finishing aspectsor a continuous film of curable gel-coat material was applied to theother pre-preg surface.

Referring to FIG. 1 this shows a fibrous reinforcing layer 1, which inthe Examples comprises carbon fiber tows; a resin layer 2 applied to alower face of the fiber tows which in the Examples which in the Examplesmay be a film formed wholly of resin material which partially penetratesthe fiber tows, or a pre-preg comprising fiber tows fully impregnatedwith resin which may also partially penetrate the overlaid fiber tows;and an openwork structure 3 of resin lines applied to the exposed drytop face of the tows and which penetrates only minimally into the fibertows.

As shown in FIG. 2, the moulding material may be made by feeding thefiber tows 1 through roller nips 4 together with top and bottommaterials 5, 6 carried on release paper supplied from reels.

The top material 5 comprises the openwork resin grid lines 3.

The bottom material 6 comprises the resin film 2, in the case ofExamples 2 and 3, or the pre-preg 2 in the case of Examples 4 and 5.

The combined layers 1-3 are driven through the nip rollers 4 which applypressure and at the same time the material is heated.

The extent of impregnation of the fiber tows 1 is controlled by theprocess conditions of speed, temperature and pressure. The exposedsurface of the fiber tows 1 can be substantially free of resin. Somecold flow of resin can occur at the boundaries of the tow layer, butthis can be restricted by selection of the materials and processconditions.

Appropriately supplemented and/or modified apparatus is used forExamples 6 and 7, involving passage of materials through roller nipswith application of heat and pressure. The dry reinforcement fibers maybe introduced as shown in FIG. 2 or alternatively can be introduced atdifferent states in the process route. Normally at least 20% of thefibers are required to be fed in at the start of the process.

Techniques for forming the prepreg layer are also well known and includesolvent-free (hot melt) processing via single or double sided resin filmimpregnation or solution processing by immersion a resin bath, meteringthe desired resin quantity and then removing solvent in an oven module.

With regard to the openwork grid lines applied to the dry fiber towsurface, possible patterns are shown FIGS. 3-9.

FIG. 3 shows diagonal lines of 8 mm width (along the web movementdirection) with 47 mm spacings therebetween.

FIG. 4 shows broken diagonal lines the sections being 40 mm long (27 mmin the web direction) with 10 mm between section ends.

FIG. 5 shows a diamond lattice arrangement, the lines being 4 mm wideand each diamond of the lattice being 78.5 mm by 40 mm respectivelylongitudinally and transversely of the web direction with a 60° diamondangle.

FIG. 6 shows transverse lines of 2 mm width, 20 mm apart.

FIG. 7 shows transverse lines of 2 mm width, 10 mm apart.

FIG. 8 shows transverse diagonal lines of 4 mm width, 59 mm apart.

FIG. 9 shows longitudinal diagonal lines of 4 mm width, 64 mm apart.

Further details are shown in the following table:

FIG. Resin gsm Dry fiber gsm Dry fiber surface area % 3 0.148 0.852 85.24 0.114 0.886 88.6 5 0.24 0.76 76 6 0.104 0.896 89.6 7 0.2 0.8 80 80.074 0.926 92.6 9 0.04 0.96 96

It will be seen that the solid resin material of the openwork resinstructure represents a minor proportion of the surface area, and indeedis essentially insubstantial relative to the overall area. The openworkresin structure is also minor, or even insubstantial, in relation to theoverall weight of resin in the moulding material. The choice ofselecting the use of continuous or discontinuous grid lines and degreeof fiber impregnation is dependent on processing factors such as theequipment used and the rheology of the resin system. It has, however,been found that discontinuous grid lines appear to be particularlysuitable for higher viscosity resins wherein low viscosity resinsfunction satisfactorily in products containing 60% dry fiber.

By way of example, using patterns such as those shown in FIGS. 3-9, thegrid lines may account for 2.1% of the total resin in the structure ofExample 2, and 6.7% in the structures of Examples 4-7.

Having thus described exemplary embodiments of the present invention, itshould be noted by those skilled in the art that the within disclosuresare exemplary only and that various other alternatives, adaptations andmodifications may be made within the scope of the present invention.Accordingly, the present invention is not limited to the above preferredembodiments and examples, but is only limited by the following claims.

1. A moulding material for use in making a moulded product, saidmoulding material comprising: a layer of fibrous reinforcing materialhaving a first side and a second side and wherein the fibrousreinforcing material consists essentially of fibers extending in acommon direction; a first layer of resin which partially impregnates thefibrous reinforcing material on said first side, said first layer ofresin providing a solid film substantially without openings therein andwherein said resin of said first layer amounts to 30 to 50% by weight ofsaid moulding material; and a further layer of resin located on saidsecond side of said fibrous reinforcing material, said further layer ofresin forming an openwork structure with a solid part and spaces throughwhich the fibrous reinforcing material is exposed and wherein said resinof said further layer amounts to 0.1 to 20% by weight of said mouldingmaterial, wherein said first and further layers of resin together amountto 30.1 to 70% by weight of said moulding material.
 2. A mouldingmaterial according to claim 1 wherein the fibrous reinforcing materialcomprises multiple side-by-side fiber tows.
 3. A moulding materialaccording to claim 1 which is an elongated structure wherein said commondirection extends longitudinally of said structure.
 4. A mouldingmaterial according to claim 1 wherein the fibrous reinforcing materialcomprises carbon fiber material.
 5. A moulding material according toclaim 1 wherein the fibrous reinforcing material comprises discontinuousfibers.
 6. A moulding material according to claim 1 wherein said firstlayer of resin comprises a pre-preg layer.
 7. A moulding materialaccording to claim 1 wherein said first layer of resin comprises aheat-curable thermosetting resin matrix.
 8. A moulding materialaccording to claim 1 wherein said first and further layers of resin areformed from the same resin.
 9. A moulding material according to claim 1wherein the solid part of said further layer of resin occupies a minorproportion of the surface area of the fibrous layer, said spaces thereincollectively making up the major part.
 10. A moulding material accordingto claim 9 wherein the solid part occupies less than 25% of the surfacearea of said second surface.
 11. A moulding material according to claim10 wherein the solid part occupies less than 4% to 24% of the surfacearea.
 12. A moulding material according to claim 1 wherein the solidpart comprises a grid pattern of solid linear elements enclosing saidspaces.
 13. A moulding material according to claim 12 wherein said gridpattern is a regular pattern whereby said spaces are of a commongeometrical shape.
 14. A moulding material according to claim 1 whereinsaid further layer of resin comprises a perforate web, perforationstherein forming the said spaces.
 15. A moulding material according toclaim 1 wherein said further layer of resin comprises separate solidparts.
 16. A moulding material according to claim 15 wherein theseparate solid parts comprise linear elements.
 17. A moulding materialaccording to claim 16 wherein the linear elements define lines.
 18. Amoulding material according to claim 17 wherein said lines are parallel.19. A moulding material according to claim 17 wherein the lines arebroken lines.
 20. A moulding material according to claim 1 wherein theamount of resin in said first layer of resin amounts to 35-40% by weightof the moulding material.
 21. A moulding material according to claim 1wherein the amount of resin in said further layer of resin amounts to0.1 to 1% by weight of the moulding material.
 22. A moulding materialaccording to claim 1 wherein the weight of the moulding material is200-800 gsm.
 23. A moulding material according to claim 1 wherein anadditional layer of material is incorporated therein.
 24. A mouldingmaterial sandwich that comprises at least one first body of mouldingmaterial according to claim 1 and a further structure applied to saidfirst layer of resin, said structure comprising further fibrousmaterial.
 25. A moulding material sandwich according to claim 24 whereinsaid further structure comprises a body of moulding material accordingto claim 1 wherein said first body of moulding material and said furtherstructure have a common first resin layer at confronting surfacesthereof, and said further resin layers are located on opposite surfacesthereof.
 26. A shaped moulded product made with a moulding materialaccording to claim
 1. 27. A moulding material according to claim 1wherein said first and further layers of resin are linked by resin partsextending through the fibrous material.
 28. A moulded product accordingto claim 26 wherein said moulded product is a wind energy blade.